Hot metal carbon silicon manganese rapid analyzer in front of the furnace

LC-TS5MHot metal carbon silicon manganese rapid analyzer in front of the furnace

1、 Instrument Introduction

LC-TS5MHot metal carbon silicon manganese rapid analyzer in front of the furnaceUsed for rapid determination of the carbon equivalent CE%, carbon content C%, silicon content Si%, manganese content Mn%, and spheroidization rate SG% of gray cast iron and ductile iron molten iron before the furnace; Predict the tensile strength of ordinary gray cast iron, etc. Non professionals can operate with simple training; Complete the detection within the waiting time of the molten iron, and then adjust the composition of the molten iron based on the automatically calculated amount of carburizer, ferrosilicon, and scrap steel, effectively guiding production practice.

2、 Main functions

1Measurement function, determination of parameters such as carbon equivalent, carbon content, silicon content, manganese content, spheroidization rate, tensile strength, Brinell hardness, etc;

2Predicting the tensile strength and Brinell hardness of gray cast iron;

3Measure the tensile strength and hardness of gray cast iron after inoculation, and predict the inoculation effect;

4After the composition determination is completed, the system automatically calculates the adjusted addition amount of the alloy based on the target values of carbon, silicon, and manganese content pre-set by the user;

5The measurement results of the carbon silicon manganese analyzer are automatically saved;

6Can reproduce historical cooling curves and measurement results at any time;

7The measurement data can be exported to EXCEL for data analysis, and can also be copied to an office computer through a USB interface for storage and analysis;

8Automatic printing is optional and can be paired with any printer to quickly print curves and measurement data.

3、 Featured Features

1After the composition determination of the carbon silicon manganese analyzer is completed, users can modify the target values according to the required carbon, silicon, and manganese content of the product and recalculate the adjustment amount of the alloy, so that the adjusted iron composition can better meet the product requirements.

2The determination of the tensile strength and hardness of gray cast iron after inoculation results in higher accuracy.

4、 Technical parameters

Analysis time: approximately 1 minute and 30 seconds

Measurement range and measurement accuracy:

Carbon equivalent CEL: 2.50-4.80%; ±0.08%

Carbon content C%: 2.30-4.20%; ±0.05％

Silicon content Si%: 0.60-3.80%; ±0.10%

Manganese content Mn%: 0.10~1.40%; ±0.15%

Spheroidization rate of 60% to 99%; ±5%

Tensile strength of 150-400MPa; ±10MPa

Hardness 100-300HB; ± 10HB