[ERICHSEN] Yilixin Plate Forming Testing Machine (Cup Convex)

NegotiableUpdate on 01/21

Model

Nature of the Manufacturer: Producers

Product Category

Place of Origin

Online Consult

Overview

The ERICHSEN Plate Forming Testing Machine (Cup Convex) 145 is a powerful and versatile plate forming testing machine. The Model 145-60/100 has two types of impact forces: 600KN and 100KN. It has strong edge pressure and cutting force, with a deep drawn sample diameter of up to 220mm. The strong edge pressure is particularly suitable for FLC experiments and bulge experiments. Real time control of stamping speed and edge pressure through manual or computer means. The control panel can display punching force, edge pressure, punch speed, and stroke. The system has security protection function. Featuring a stamping speed of up to 3

Product Details

Meet the test standards:
National standard GB 15825: Various tests
Cup convexity test meets EN ISO, EURONOM, BS, NF, GOST, UNI, UNE
Deep pull cup test
The deep hole expansion test meets the requirements of Siebel and Pomp (KWI)
Hole enlargement test ISO 16630
FLC experiment meets acc. to ISO 12004

Technical Specifications:

145-60 145-100

Pressure: maximum 600KN, maximum 1000KN

Edge pressure: maximum 600KN maximum 1000KN maximum

Shear force of deep tensile test specimen: maximum 700KN maximum 1000KN maximum

Deep drawing punch diameter: maximum 100mm, maximum 100mm

Deep stroke: 150mm (250mm optional) 150mm (250mm optional)

Edge stroke: 38mm 38mm

Deep cup ejection stroke: 150mm (250mm optional) 150mm (250mm optional)

Deep drawn sample diameter: 220mm 220m

Deep pulling speed: 750mm/Min 750mm/Min

Thickness of cup convex sample: 0.1-6.0mm 0.1-6.0mm

Deep drawn sample thickness: 0.2-3.0mm 0.2-6.0mm

Thickness of enlarged hole specimen: 0.2-3.0mm 0.2-3.0mm

FLC punch diameter: maximum 100mm, maximum 100mm

Bulge test punch diameter: maximum 100mm, maximum 100mm

Testing methods: Erichsen cup bulge test, deep pull test, hole expansion test, square cup test, FLC curve test, LDH test, bulge test, lubrication test, 550 ℃ high temperature deep pull test, high-speed deep pull test, Fukui test, Olsen, Swift test, reverse tensile test, precision cutting experiment, hardness test, tensile test, etc.